RTP EMI 1060
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1Y1gya_RTP-EMI-1060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.9 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength | 53.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength | 85.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.35 mm) | 370 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 150 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 54.4 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 7mil/in.Wear Factor, K, ASTM D-3702, in³min/ft/lb/hr x 10-10: 120Coefficient of Friction, Static, ASTM D-3702: 0.14Coefficient of Friction, Dynamic, ASTM D-3702: 0.15The wear factor and coefficient of frictions were both tested on a Falex Model No. 6 Wear Testing Machine AT 50 fpm, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness.The value listed as flammability, UL 94, was tested in accordance with RTP test standards. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 - 271 | °C | |
| Middle Temperature | 232 - 271 | °C | |
| Front Temperature | 232 - 271 | °C | |
| Mold Temperature | 37.8 - 121 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 202A GB 15 | RTP Company | Nylon 6 | RTP |
| TOTAL Polyethylene HDPE 6410 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| Wah Hong BMC BUG-3101C Optical | Wah Hong Industrial Corp. | TS, Unspecified | Wah Hong BMC |
| Borealis PE FG5223 | Borealis AG | LLDPE | Borealis PE |
| MACOMASS TPE MM-TPE V 5010 | MACOMASS Verkaufs AG | TPE | MACOMASS TPE |