SABIC® LLDPE 6821NE
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1Xg32Z_SABIC-LLDPE-6821NE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LLDPE 6821NE is a hexene linear low density polyethylene. Films made from this resin exhibit good tensile strength, stiffness, dart drop impact strength, tear strength and hottack properties. The suffix E denotes European origin. Application Typical applications for SABIC® LLDPE 6821NE are heavy duty bags, lamination films, agriculture films, stretch wrap films, frozen food packaging and other applications requiring high impact strength and tear resistance. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 220 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 250 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 12.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 13.5 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 45.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 38.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 600 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 750 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (50.0 µm) | 300 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance - Blown Film (50.0 µm) | 700 | J/m | Internal method |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 80.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 330.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 111 | °C | ISO 306/A |
| Melting Temperature (DSC) | 125 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 15 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film of 50 µm and BUR = 2 has been produced on Kiefel IBC with 140 kg/h. Die size 200 mm, die gap 2.7 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PVC S7106 | Sasol Polymers | PVC, Unspecified | Sasol Polymers PVC |
| Vipel® F282-AAC-19 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| DAPCO™ 3008 | Cytec Industries Inc. | Epoxy | DAPCO™ |
| IDI SMC E5V-204 | IDI Composites International | TS, Unspecified | IDI SMC |
| Hostacom TRC 787N E C12616 | LyondellBasell Industries | PP Copolymer | Hostacom |