HANWHA LLDPE 3304
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1XZKw0_HANWHA-LLDPE-3304.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LLDPE 3304 is manufactured by Spherilene process and designed for general purpose film. LLDPE 3304 has well balanced property of mechanical property and processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 21.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 900 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 30 µm | 40.2 | MPa | ASTM D882 |
| TD : Break, 30 µm | 36.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 550 | % | ASTM D882 |
| TD : Break, 30 µm | 700 | % | ASTM D882 |
| Dart Drop Impact (30 µm) | 130 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 30.0 µm | 117.7 | kN/m | ASTM D1004 |
| TD : 30.0 µm | 122.6 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 |
| Peak Melting Temperature | 125 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm) | 12 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3Optimum Gage Range: 0.03 to 0.1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ML-1690B BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| Braskem PP R7050-02N | Braskem Europe GmbH | PP Random Copolymer | Braskem PP |
| Hostaform® C 13031 LS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Paxon™ BA54-030 | ExxonMobil Chemical | HDPE Copolymer | Paxon™ |
| Thermec N™ 4340R30F4 | Technical Polymers, LLC | PPA | Thermec N™ |