Innothane® IE-3040
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1WuZrS_Innothane-IE-3040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-3040 is a polyethylene-like polyurethane formulated for hand-batch processing, roto-casting or vacuum cast methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. It has excellent green strength yielding enhanced demold characteristics. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.05 | g/cm³ | |
| Cured | 1.08 | g/cm³ | |
| Base Resin | 1.21 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 469 | MPa | ASTM D790 |
| Flexural Strength | 21.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 85.0 | °C | |
| 1.8 MPa, Unannealed | 61.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 70 Mix Ratio by Volume: 61 | ||
| Demold Time | 60 to 120 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.075 | Pa·s | |
| 25°C 2 | 0.30 | Pa·s | |
| 25°C 3 | 0.90 | Pa·s | |
| Curing Time 4 | 25 | hr | |
| Gel Time | 4.0 to 6.0 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 55 to 65 | ASTM D2240 | |
| Tensile Strength | 23.4 | MPa | ASTM D638 |
| Tensile Elongation at Break | 55 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hour at 77°F + 1 hour at 150"F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SWANCOR Epoxy 977 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| ESTADIENE 0420 HHT | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| LUVOCOM® 1301-7449 | Lehmann & Voss & Co. | PPS | LUVOCOM® |
| PLUSTEK PB300G6 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| Sylvin 5170-85 Yellow 405 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |