LNP™ THERMOCOMP™ EC005 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1Wfazg_LNPTHERMOCOMPEC005compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP EC005 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features include : Electrically Conductive. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 24 hours | 0.30 - 0.50 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.10 - 0.30 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 191 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 13600 | MPa | ISO 178 |
| Flexural Stress | 243 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 214 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 354 - 366 | °C | |
| Front Temperature | 366 - 377 | °C | |
| Processing (Melt) Temp | 360 - 366 | °C | |
| Mold Temperature | 121 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinkral® PD D 232/M4 | Versalis S.p.A. | ABS | Sinkral® |
| VESTOLIT® P 1352 K | VESTOLIT GmbH & Co. KG | PVC Homopolymer | VESTOLIT® |
| Vi-Chem PVC VDM87-80E-XXXX | Vi-Chem Corporation | PVC, Rigid | Vi-Chem PVC |
| HiFill FR® PA6/6 GF25 FR-N IM BK | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |
| ICORENE® 3440 | ICO Polymers SA, A Division of A. Schulman | PE Copolymer | ICORENE® |