Kinta NB6615G
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Kinta Technology (Hong Kong) Co., Ltd. |
| Trademark: | Kinta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1W77s1_KintaNB6615G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kinta NB6615G is a polyamide 66 (nylon 66) product, which contains a 15% glass fiber reinforced material. It is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.00 mm) | 0.50 - 1.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 108 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus 3 | 5000 | MPa | ASTM D790 |
| Flexural Strength 4 | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 5.50 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 235 | °C | ASTM D648 |
| Melting Temperature | 260 | °C | DSC |
| CLTE - Flow | 2.0E-5 - 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dissipation Factor 5(23°C, 1 MHz) | 0.040 | ASTM D150 | |
| Arc Resistance | 110 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 250 - 270 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Injection Pressure | 100 - 160 | MPa |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2204 LF | RTP Company | PEEK | RTP |
| Celstran® PA6-GF40-03 | Celanese Corporation | Nylon 6 | Celstran® |
| Jackdaw PP EW16NT6686 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |
| Lion Idemitsu Composites PPS C-140SF | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Sylvin 8260-80 White 1439 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |