Generic PP Homopolymer - Unspecified
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1VaHNn_Generic-PP-Homopolymer---Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - Unspecified This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.03 - 1.22 | g/cm³ | ASTM D792 |
| 23°C | 0.780 - 2.80 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 - 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.20 - 0.92 | % | ASTM D955 |
| 23°C | 1.1 - 1.7 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 90 - 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1000 - 5500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 24.5 - 88.9 | MPa | ASTM D638 |
| Fracture, 23°C | 14.8 - 22.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 3.0 - 10 | % | ASTM D638 |
| Fracture, 23°C | 1.0 - 100 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3420 - 7100 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 33.8 - 116 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.0 - 6.1 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 4.7 - 20 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 25 - 82 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 300 - 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 155 - 162 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 55.0 - 131 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 40.0 - 107 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 50.0 - 161 | °C | ISO 306 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 85.1 | °C | |
| Processing (Melt) Temp | 204 - 240 | °C | |
| Mold Temperature | 32.3 - 33.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - UnspecifiedThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Propionate 350E0096912 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Texalan® 4 Series 490A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 4 Series |
| Petrothene® NA480145 | LyondellBasell Industries | LDPE | Petrothene® |
| ISOTHANE® 8101 | Great Eastern Resins Industrial Co., Ltd. (GRECO) | TPU, Unspecified | ISOTHANE® |
| ALTECH® PA6 + ASA A 4010/621 MR10 IM UV | ALBIS PLASTIC GmbH | ASA+Nylon | ALTECH® PA6 + ASA |