Nylene® NX1440 HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Custom Resins Group |
| Trademark: | Nylene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1U5Y1Y_Nylene-NX1440-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylene NX1440 is a high viscosity, fast cycling molding resin. Crystallization initiators provide fast molding cycles through rapid melt set-up. Parts molded from NX1440 have better dimensional stability at moisture equilibrium than parts molded from conventional nylon. Nylene NX1440 provides for an excellent balance between stiffness and toughness. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.90 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.5 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 75.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 25 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2900 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 82.2 | °C | ASTM D648 |
| Melting Temperature | 216 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Shot Size | 25 to 75 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 221 to 246 | °C | |
| Middle Temperature | 227 to 260 | °C | |
| Front Temperature | 238 to 271 | °C | |
| Nozzle Temperature | 238 to 271 | °C | |
| Processing (Melt) Temp | 238 to 271 | °C | |
| Mold Temperature | 48.9 to 93.3 | °C | |
| Injection Pressure | 27.6 to 82.7 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 20.7 to 62.1 | MPa | |
| Back Pressure | 0.00 to 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1403 | RTP Company | PESU | RTP |
| SAXAMID™ 226F10 | SAX Polymers | Nylon 66 | SAXAMID™ |
| WPP PP PPH2CF2-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| APEX® 94-A0098A-70 | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina IVORY PVC COMPOUND 75920-35/1-B-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |