LNP™ LUBRICOMP™ HX00059 compound
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ToqZW_LNP-LUBRICOMP-HX00059-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP * LUBRICOMP* HX00059 is a compound based on PA 11 resin, containing a Proprietary Lubricant. Added features include: Internally Lubricated. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 2.6 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 41.0 | MPa | |
| Break | 41.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 120 | % | |
| Break | 230 | % | |
| Flexural Modulus 1 | 300 | MPa | ISO 178 |
| Flexural Stress | 12.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 120 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 48.0 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.1E-4 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.9E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 199 to 210 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 227 to 260 | °C | |
| Mold Temperature | 43.3 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE EE-1230N | Teknor Apex Company | TPE | Sarlink® TPE |
| Andur 9000-AP/Curene® 280 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Fainplast PVC FK 91 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Dugdale PVC Rigid Extrusion Black Compound | Dugdale Plc | PVC, Rigid | Dugdale PVC |
| Karina NATURAL PVC COMPOUND -E 900-25/ 1-AYR-IS-LF(*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |