Orgalloy® RS 6015 ES T6L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Arkema |
| Trademark: | Orgalloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ThX7m_Orgalloy-RS-6015-ES-T6L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Orgalloy® RS 6015 ES T6L is a Polyamide 6 (Nylon 6) product filled with filler. It can be processed by blow molding, extrusion, or profile extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: heat resistant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1200 | 1200 | kg/m³ | ISO 1183 1 |
| Melt volume-flow rate (235°C/5.0 kg) | 0.500 | -- | cm³/10min | ISO 1133 2 |
| Water Absorption | ISO 62 3 | |||
| Saturation | 2.8 | -- | % | |
| Equilibrium | 1.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile modulus | -- | 2850 | MPa | ISO 527-2 4 |
| Tensile Stress (Break) | -- | 75.0 | MPa | ISO 527-2 5 |
| Tensile Strain (Break) | -- | 6.5 | % | ISO 527-2 6 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 7 | |||
| -30°C | -- | 5.00 | kJ/m² | |
| 23°C | -- | 13.5 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 8 | |||
| 0.45 MPa | 210 | -- | °C | |
| 1.8 MPa | 175 | -- | °C | |
| Melting Temperature 9 | 220 | -- | °C | ISO 11357-3 10 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface resistivity | -- | > 1.0E+15 | ohms | IEC 60093 11 |
| Volume resistivity | -- | > 1.0E+13 | ohms·m | IEC 60093 12 |
| Electric strength | 35 | 35 | kV/mm | IEC 60243-1 13 |
| Relative Permittivity | IEC 60250 14 | |||
| 100 Hz | -- | 3.00 | ||
| 1 MHz | -- | 3.00 | ||
| Dissipation Factor | IEC 60250 15 | |||
| 100 Hz | -- | 0.063 | ||
| 1 MHz | -- | 0.024 | ||
| Comparative tracking index | -- | 600 | IEC 60112 16 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | HB | -- | ISO 1210 17 | |
| Burning Behav. at thickness h (3.20 mm) | HB | -- | ISO 1210 18 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | 10 °C/min |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FP62E13 | The Matrixx Group, Inc. | Nylon 6 | Matrixx |
| TRILOY® TP210T | Samyang Corporation | PC+ABS | TRILOY® |
| Witcom PBT 6G/2L3 | Witcom Engineering Plastics B.V. | PBT | Witcom PBT |
| LNP™ LUBRILOY™ KL201 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRILOY™ |
| PARAPET HR-F | Kuraray Co., Ltd. | Acrylic (PMMA) | PARAPET |