Nypol® PA A3 G10 N8 NTLA014 NR386
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ST5AF_Nypol-PA-A3-G10-N8-NTLA014-NR386.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural reinforced with 10% of fiberglass and 8% graphite, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.20 to 1.24 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 to 1.2 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.7 | -- | % | ASTM D570 |
| Ash Content | ||||
| Fiberglass | 8.0 to 12 | -- | % | ASTM D2584 |
| Graphite | 6.00 to 10.0 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 120 | 85.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 7.0 | % | ASTM D638 |
| Flexural Modulus | 4900 | 2770 | MPa | ASTM D790 |
| Flexural Strength | 167 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 50 | 55 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 240 | -- | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+13 | ohms·cm | ASTM D257 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer Pipe PP 410/401 | Polylink Polymers (India) Ltd. | PP, Unspecified | Polylink Polymer |
| RTP 107 | RTP Company | PP, Unspecified | RTP |
| Spartech Polycom SC7-70915 | Spartech Polycom | PC | Spartech |
| Spartech Polycom SCR7F-7015AR | Spartech Polycom | PC | Spartech |
| Shida 2512 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | TPE | Shida |