Iupiace® EHM1010A
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupiace® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1SCaGi_Iupiace-EHM1010A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Iupiace® EHM1010A is a Polyphenylene Ether + PS (PPE+PS) material. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Iupiace® EHM1010A: Antistatic. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.55 to 0.75 | % | |
| Flow : 3.20 mm | 0.55 to 0.75 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3700 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 64.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.2 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 101 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 155 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 5.3E-5 | cm/cm/°C | |
| Transverse | 5.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0E+5 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 290 to 310 | °C | |
| Middle Temperature | 310 to 330 | °C | |
| Front Temperature | 310 to 330 | °C | |
| Nozzle Temperature | 310 to 330 | °C | |
| Mold Temperature | 110 to 130 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen D60P | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| TOTAL Polystyrene Crystal CX5243 | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| UBE Polyethylene F023 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Zytel® ST7301 NC010 | DuPont Performance Polymers | Nylon 6 | Zytel® |
| Huaxia Shenzhou PVDF DS204 | Shandong Huaxia Shenzhou New Material Co., Ltd. | PVDF | Huaxia Shenzhou |