Infino CF-1070
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1RX3mN_Infino-CF-1070.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High-impact material for the exterior material of mobile phone |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 13 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 59.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2000 | MPa | ASTM D790 |
| -- 3 | 2100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 83.0 | MPa | ASTM D790 |
| -- 5 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 60 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 690 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 540 | J/m | ASTM D256 |
| 23°C 7 | 65 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 138 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 2.50 mm | V-2 | ||
| 3.00 mm | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 2.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 152 | RTP Company | PP, Unspecified | RTP |
| Advanced Composites ATX639MX2N | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| Exelene® HDPE 5502M | Montachem International, Inc. | HDPE | Exelene® HDPE |
| Haysite Plastics H261 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| DAI-EL™ LT-304 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |