Trexprene® A55NI-HF
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1QKa3u_Trexprene-A55NI-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A55NI-HF is a natural heat stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This material can be processed using Extrusion, Injection, Blow Molding equipment, or other melt processing. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 to 1.00 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 52 to 58 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Across Flow : 100% Strain | 1.80 | MPa | |
| Flow : 100% Strain | 2.20 | MPa | |
| Tensile Stress 2 | ISO 37 | ||
| Across Flow : Break | 4.80 | MPa | |
| Flow : Break | 2.80 | MPa | |
| Tensile Elongation 3 | ISO 37 | ||
| Across Flow : Break | 400 | % | |
| Flow : Break | 250 | % | |
| Tear Strength 4 | ISO 34-1 | ||
| Across Flow | 18 | kN/m | |
| Flow | 15 | kN/m | |
| Compression Set | |||
| 70°C, 24 hr | 30 | % | ASTM D395B |
| 125°C, 70 hr | 40 | % | ASTM D395B |
| 70°C, 24 hr 5 | 30 | % | ISO 815 |
| 125°C, 70 hr 6 | 40 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (110°C, 1000 hr) | -5.0 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (110°C, 1000 hr) | -10 | % | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | -56.0 | °C | ASTM D746 |
| Type B | -56.0 | °C | ISO 812 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 19 | mm/min | ISO 3795 |
| Fogging - Dry Fog | 82 | % | SAE J1756 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Color Fastness - to Light 7 | Delta E < 3.0 | ||
| Odor Rating 8 | > 7.00 | ||
| Ozone Resistance 9(40°C) | 0 Rating | ISO 1431-1 |
| Note Message | |
|---|---|
| 1 . | Type 1, 500 mm/min |
| 2 . | Type 1, 500 mm/min |
| 3 . | Type 1, 500 mm/min |
| 4 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 5 . | Type A |
| 6 . | Type A |
| 7 . | SAE J2412, ISO 105-B06, Cond. 5, 1,240.8 kJ/m² |
| 8 . | GMW3205 Code B |
| 9 . | 100 pphm, Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8270 HS | BASF Corporation | Nylon 6 | Ultramid® |
| Axplas® MEP53 0000 | Axion Polymers | TP, Unspecified | Axplas® |
| Epolene® N-15P | Westlake Chemical Corporation | PP Homopolymer | Epolene® |
| COSMOPLENE® AX161S | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| LNP™ THERMOCOMP™ DF004P compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |