Plaslube® NY-1/SI/2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1Q8zN2_Plaslube-NY-1-SI-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube®NY-1/SI/2 is a polyamide 66 (nylon 66) product,. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: architectural applications. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 74.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.5 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- | 100 | MPa | ASTM D790 |
| Fracture, 23°C | 100 | MPa | ASTM D790 |
| Compressive Strength | 89.6 | MPa | ASTM D695 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.090 | ASTM D1894 | |
| With steel-static | 0.090 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 79.4 | °C | ASTM D648 |
| CLTE - Flow | 8.1E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Coefficient of Friction, Static, Thrust washer, 40psi, ambient temp.: 0.09Coefficient of Friction, Dynamic, Thrust washer, 40psi, 50 ft/min, ambient temp.: 0.09Limiting PV, Thrust washer, 100 FPM, ambient temperature: 6E3Compressive Strength, ASTM D695, 73°F: 13000 psi |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 282 - 288 | °C | |
| Middle Temperature | 282 - 288 | °C | |
| Front Temperature | 277 - 282 | °C | |
| Nozzle Temperature | 271 - 277 | °C | |
| Processing (Melt) Temp | 271 - 293 | °C | |
| Mold Temperature | 54.4 - 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well ventedMoisture Content, as received: Product is packaged at 0.2% or less.Recomended Max Moisture: 0.12% down to 0.08% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1305 TFE 10 | RTP Company | PPS | RTP |
| SABIC® STAMAX 20YK270 resin | SABIC Innovative Plastics | PP, Unspecified | SABIC® STAMAX |
| RTP 106CC | RTP Company | PP Homopolymer | RTP |
| Ultramid® B40 | BASF Corporation | Nylon 6 | Ultramid® |
| LUVOCOM® 1105-8592 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |