LNP™ THERMOCOMP™ RF0049SP compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1Q7cUG_LNP-THERMOCOMP-RF0049SP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF0049SP is a compound based on Nylon 66 containing 20% Glass Fiber. Added features of this grade include: Flame Retardant, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RF-1004 FR HS Product reorder name: RF0049SP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 to 0.60 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9610 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 1 | 140 | MPa | ASTM D638 |
| Break | 140 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 2 | 2.3 | % | ASTM D638 |
| Break 3 | 2.4 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 8650 | MPa | ASTM D790 |
| -- 5 | 8170 | MPa | ISO 178 |
| Flexural Strength 6(Break, 50.0 mm Span) | 203 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 67 | J/m | ASTM D256 |
| 23°C 7 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 600 | J/m | ASTM D4812 |
| 23°C 8 | 36 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 2.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 255 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 253 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 241 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 235 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 3800-65NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| EVERLON® TY-45 | Ever Polymer Co., Ltd. | SBS | EVERLON® |
| Flontech® FT-GL15-M5-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Epic Urethane S7144 | Epic Resins | PUR, Unspecified | Epic Urethane |
| Karina WHITE PVC COMPOUND -E 830-10/150-Y-ERYB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |