Celcon® MR90B
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celcon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1PUg8e_Celcon-MR90B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celcon® MR90B is a standard flow specialty media resistant grade developed for improved bleach resistance. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 2.2 | % | ISO 294-4 |
| Flow direction | 2.2 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 11 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.1 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 110 | kJ/m² | ISO 179/1eU |
| 23°C | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 8.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 190 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 180 - 190 | °C | |
| Nozzle Temperature | 180 - 200 | °C | |
| Processing (Melt) Temp | 180 - 200 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 180 to 200°CZone 4 Temperature: 180 to 200°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2740 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Vipel® K022-CCK-18 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| FARBOSET® 1190 | Cosmic Plastics, Inc. | Epoxy | FARBOSET® |
| Huafon JF-P-4170T / JF-I-4118 (outsole) | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| Luranyl® KR 2403 G4 TW 26343 | ROMIRA GmbH | PPE+PS | Luranyl® |