Order Products : sales@su-jiao.com
AIE PPO 9010F-S100C
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | AIE PPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1PGIBz_AIE-PPO-9010F-S100C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AIE PPO 9010F-S100C is a Polyphenylene Ether + PS (PPE+PS) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of AIE PPO 9010F-S100C are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 48.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Flexural Stress | 79.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 19 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 123 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 103 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 30.0 to 80.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® PC2540.U | Guangdong Silver Age Sci & Tech. Co., Ltd | PC+ABS | SILVER® |
| ALCUDIA® EVA PA-442 | REPSOL | EVA | ALCUDIA® EVA |
| PELPRENE™ S2002 | TOYOBO America, Inc. | TPEE | PELPRENE™ |
| Badatech HT® PEEK CF10/GR10/TF10 | Bada AG | PEEK | Badatech HT® |
| LEXAN™ EXL1434 resin | SABIC Innovative Plastics | PC | LEXAN™ |