ASTALOY™ PC/ABS MC300
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1NVks5_ASTALOY-PC-ABS-MC300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALOY™ PC/ABS MC300 is a general purpose alloy of ABS and Polycarbonate and is designed for injection moulding applications requiring a balance of high impact toughness, product rigidity, high heat resistance and mouldability. Typical applications in the automotive area include coloured interior doorhandles as well as instrument panel structural components and panels. Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: ASTALOY™ PC/ABS MC300U ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/3.8 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 48.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 77.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 380 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 35.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 90.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 95.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 102 | °C | |
| Vicat Softening Temperature | 122 | °C | ASTM D1525 5 |
| CLTE - Flow | 7.6E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 650 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 225 to 245 | °C | |
| Middle Temperature | 235 to 255 | °C | |
| Front Temperature | 245 to 265 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1307 MS 5 | RTP Company | PPS | RTP |
| Valtec HP423M | INDELPRO, S.A. de C.V. | PP Homopolymer | Valtec |
| PULSE™ XT50 | Trinseo | PC+ABS | PULSE™ |
| Thermec S™ 6250R50 | Technical Polymers, LLC | PPS | Thermec S™ |
| NORYL™ WCD933 resin | SABIC Innovative Plastics | PPE+TPE | NORYL™ |