SABIC® COHERE™ 8102
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® COHERE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1MgbFd_SABICCOHERE8102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® COHERE™ 8102 is a ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of general purpose and high performance LLDPE blown film applications and has excellent processability. SABIC® COHERE™ 8102 does not contain Slip and Antiblock. Applications Typical application for SABIC® COHERE™ 8102 is low temperature sealing layer for high value packaging (low SIT, seal through contamination, toughness improvement). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.902 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 68.0 | MPa | ASTM D882 |
| 1% secant, TD | 76.0 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 47.0 | MPa | ASTM D882 |
| TD : Fracture | 42.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 600 | % | ASTM D882 |
| TD : Fracture | 620 | % | ASTM D882 |
| Dart Drop Impact 1 | > 1000 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 10 | g | ASTM D1922 |
| TD | 17 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 100 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 4.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blown Film Melt Temperature | 180 - 200 | °C | |
| Blow-up Ratio | 2.00 - 3.00 | ||
| Properties have been measured on blown film of 50 µm and BUR = 2.5 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® H3KC | BASF Leuna GmbH | Nylon 6 | Miramid® |
| Sup-tech A706SH | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon, Unspecified | Sup-tech |
| Witcom PC 3C-EM-MR Black | Witcom Engineering Plastics B.V. | PC | Witcom PC |
| Dow ENDURANCE™ HFDA-0587 BK | The Dow Chemical Company | TP, Unspecified | Dow ENDURANCE™ |
| ICORENE® N9501 | ICO Polymers EMEA, A Division of A. Schulman | SAN | ICORENE® |