KOCETAL® UR302LO
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOCETAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1MgN5l_KOCETAL-UR302LO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOCETAL®UR302LO is a polyoxymethylene (POM) copolymer product,. It is available in North America, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.24 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 52.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 85 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2000 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 73.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 90 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, not annealed | 150 | °C | ASTM D648A |
| 1.8 MPa, not annealed | 90.0 | °C | ASTM D648A |
| Melting Temperature | 166 | °C | ASTM D1525 |
| CLTE - Flow | 1.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Formaldehyde Level | ppm | VDA 275 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX 2050 W G3 | Taro Plast S.p.A. | PBT+PET | TAROLOX |
| NuSil MED-2245 | NuSil Technology | Rubber | NuSil |
| Hostacom X 4305 LS71 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Hylac® GP55G10 | Ravago Manufacturing Americas, LLC | ABS | Hylac® |
| LNP™ LUBRICOMP™ UFL269SA compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |