NAXELL™ PC210MR
| Category: | PC , Polycarbonate |
| Manufacturer: | MRC Polymers, Inc. |
| Trademark: | NAXELL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1MS0Fa_NAXELL-PC210MR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC210HR is available in black color only. Further information and details are available upon request. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, 3.18 mm) | 62.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C, 3.18 mm) | 50 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.18 mm) | 2270 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.18 mm) | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 132 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 120 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ C140GP | Mando Advanced Materials Co., Ltd. | LCP | SEPAZ™ |
| THERMOLAST® K TC9FRN (Series: FR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Wellamid® NY1599-BK11 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| NuSil MED-5440 | NuSil Technology | Silicone Rubber, LSR | NuSil |
| LNP™ COLORCOMP™ A1000H compound | SABIC Innovative Plastics | ABS | LNP™ COLORCOMP™ |