EVALENE® PP PHF0221
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | JG Summit Petrochemical Corporation |
| Trademark: | EVALENE® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1Lpwf9_EVALENE-PP-PHF0221.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PP is used in making films, adhesive tapes, cigarette and candy wrappers, cosmetics, pharmaceutical and food packaging materials. High Clarity. Hot-Fill Applications. Living Hinge. Evalene® Random Copolymer PP is widely used in the following applications: Injection Molding: Houseware, lunch boxes and pencil cases with "living hinges" Blow Molding: Baby bottles, bottles for juice, tea, water, medicine, and cosmetics Good Economics. Hot-Fill Applications. Excellent Film Clarity. Good Tenacities. Evalene® Homopolymer PP is the material of choice for a host of applications: Tape Extrusion: Woven bags for rice, cement and industrial chemicals Films: Bi-axially oriented, cast and inflation films for tapes, packaging, and labels Injection Molding: Monobloc furnitures, pails, houseware, containers, toys, caps Thermoforming: Fastfood containers, mineral water cups |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, Injection Molded) | 97 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant 1(Injection Molded) | 1400 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, Injection Molded) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Yield, Injection Molded) | 22 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 4(Injection Molded) | 1270 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Injection Molded) | 89.0 | °C | ASTM D648 |
| Peak Melting Temperature 5 | 163 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 230 - 240 | °C |
| Extrusion instructions |
|---|
| Chill Roll Temperature: 20 to 25°C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 10°C/min, 2nd heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9960 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TPSiV™ 4000-60A | Multibase, A Dow Corning Company | TPSiV | TPSiV™ |
| Baydur® 641 IBS (25 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Fainplast PVC GK 80 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Karina NATURAL PVC COMPOUND -E 900-25/ 1-AYR-IS-LF(*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |