Resinoid 1328
| Category: | Phenolic , Phenolic |
| Manufacturer: | Resinoid Engineering Corporation |
| Trademark: | Resinoid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1IkU8p_Resinoid-1328.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Resinoid 1328 is a glass reinforced, two-step phenolic molding compound. It was specifically developed for applications requiring exceptional tensile strength such as grinding wheels. Resinoid 1328 exhibits excellent electrical and thermal properties as well as dimensional stability. This material comes in pelletized from and is suitable for injection, transfer or compression molding. It can be preformed on automatic equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.96 | g/cm³ | ASTM D792A, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.20 | % | ASTM D955 |
| Flow direction | 0.20 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr | 0.12 | % | ASTM D570 |
| 23°C, 24 hr | 0.12 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| E scale | 90 | ASTM D785 | |
| Class m | 112 | ASTM D785 | |
| M scale | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 34.9 | MPa | ASTM D638 |
| Yield | 34.8 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 15200 | MPa | ASTM D790 |
| -- | 15000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 88.3 | MPa | ASTM D790 |
| -- | 88.0 | MPa | ISO 178 |
| Compressive Strength | 166 | MPa | ASTM D695, ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 57 | J/m | ASTM D256A |
| -- | 5.6 | kJ/m² | ISO 180/2A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 316 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 315 | °C | ISO 75-2/A |
| CLTE - Flow | |||
| -- | 2.6E-5 | cm/cm/°C | ASTM D696 |
| -- | 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 13 | kV/mm | ASTM D149, IEC 60243-1 |
| Arc Resistance | 204 | sec | ASTM D495 |
| Additional Information |
|---|
| DTUL @264 psi - Unannealed, ASTM D648: >600°FHDT A (1.80 MPa) Unannealed, ISO 75A-1-2: >315°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T & T Marketing TPE 6187 | T & T Marketing, Inc. | TPV | T & T Marketing |
| Trexprene® A64CI | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Witcom PC/ABS AS-S-LM | Witcom Engineering Plastics B.V. | PC+ABS | Witcom PC/ABS |
| ADENE NCQAG | A.D. Compound spa | PP Copolymer | ADENE |
| Gallonprene® GP210-6511 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |