POLIMAXX 1111NXBA4
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | IRPC Public Company Limited |
| Trademark: | POLIMAXX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1HwcTQ_POLIMAXX-1111NXBA4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 1111NXTA8 is a PP Homopolymer with 20% Barium Sulfate filler for injection molding process, featuring medium melt flow, high flexural modulus and high heat resistance. It is suitable for electrical appliances. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 584 mm) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 33.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 30 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1960 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 43.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 3.04 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 120 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® N-324 | Matrix Polymers | LMDPE | REVOLVE® |
| THERMOLAST® K TF4AAB (Series: FC/HE/tl) | KRAIBURG TPE | TPE | THERMOLAST® K |
| ACCUTECH™ HP0336G25C002L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| BJB Polyurethane TC-670 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| LNP™ LUBRICOMP™ AL003 compound | SABIC Innovative Plastics | ABS | LNP™ LUBRICOMP™ |