ECO PELLET® LA17C
| Category: | PLA+ABS , Polylactic Acid + ABS |
| Manufacturer: | UMG ABS, Ltd. |
| Trademark: | ECO PELLET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1HEKqn_ECO-PELLET-LA17C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ECO PELLET® LA17C is a Polylactic Acid + ABS (PLA+ABS) material. It is available in Asia Pacific or North America for injection molding. Important attributes of ECO PELLET® LA17C are:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.28 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (200°C/10.0 kg) | 59.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.80 to 1.1 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 106 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 40.0 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 3500 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 67.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 21 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 78.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 150 to 190 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 180 to 220 | °C | |
| Nozzle Temperature | 170 to 210 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 100 | °C | |
| Injection Pressure | 70.0 to 130 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 5.00 to 10.0 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEDUR® L 9214-1 | ALBIS PLASTIC GmbH | PPS | TEDUR® |
| SUMIKASUPER® LCP E6109F | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Delta ATL H5 | Delta Polymers | Acetal (POM) Homopolymer | Delta |
| Gallonprene® GP210-6011 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Sylvin 6231-90 Blue 8465 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |