Ultramid® 8233G HS BK-106 Datasheet,Nylon 6,BASF Corporation-SHANGHAI SUSHENG

Message
Ultramid 8233G HS BK-106 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. This balance of engineering properties in combination with excellent processability make it ideal in applications replacing metal, resulting in an overall cost and weight savings. Applications Ultramid 8233G HS BK-106 is generally recommended for applications such as weed trimmer components, gears, automotive window hardware, electrical connectors and coil bobbins and all external parts exposed to the environment.

General Information
Filler / Reinforcement	Glass Fiber, 33% Filler by Weight
Additive	Heat Stabilizer
Features	Good Dimensional Stability Good Processability Good Stiffness Good Weather Resistance Heat Stabilized High Strength
Uses	Automotive Applications Automotive Exterior Parts Bobbins Connectors Gears Metal Replacement
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Appearance	Black
Forms	Pellets
Processing Method	Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity	1.39	--	g/cm³	ASTM D792, ISO 1183
Molding Shrinkage - Flow (3.18 mm)	0.30	--	%
Water Absorption
24 hr	1.1	--	%	ASTM D570
23°C, 24 hr	1.1	--	%	ISO 62
Saturation	6.4	--	%	ASTM D570
Saturation, 23°C	6.4	--	%	ISO 62
Equilibrium, 50% RH	1.8	--	%	ASTM D570
Equilibrium, 23°C, 50% RH	1.8	--	%	ISO 62

Hardness	Dry	Conditioned	Unit	Test Method
Rockwell Hardness (R-Scale)	121	--		ASTM D785

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus				ISO 527-2
-40°C	10400	11500	MPa
23°C	10500	7700	MPa
80°C	4660	4600	MPa
121°C	4020	4200	MPa
Tensile Strength
Break, -40°C	210	215	MPa	ASTM D638, ISO 527-2
Break, 23°C	160	100	MPa	ASTM D638
Break, 80°C	85.0	70.0	MPa	ASTM D638, ISO 527-2
Break, 121°C	70.0	60.0	MPa	ASTM D638, ISO 527-2
Break, 23°C	155	100	MPa	ISO 527-2
Tensile Elongation
Break, -40°C	3.0	2.5	%	ASTM D638
Break, 23°C	2.0	6.0	%	ASTM D638, ISO 527-2
Break, 80°C	7.0	6.5	%	ASTM D638
Break, 121°C	7.0	6.5	%	ASTM D638
Flexural Modulus
23°C	8990	--	MPa	ASTM D790
23°C	8700	--	MPa	ISO 178
Flexural Strength
23°C	280	--	MPa	ASTM D790
23°C	225	--	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179
-30°C	5.5	--	kJ/m²
23°C	8.0	--	kJ/m²
Charpy Unnotched Impact Strength (23°C)	55	--	kJ/m²	ISO 179
Notched Izod Impact
23°C	110	--	J/m	ASTM D256
-40°C	6.0	--	kJ/m²	ISO 180
23°C	8.5	--	kJ/m²	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed	218	--	°C	ASTM D648
0.45 MPa, Unannealed	215	--	°C	ISO 75-2/B
1.8 MPa, Unannealed	208	--	°C	ASTM D648
1.8 MPa, Unannealed	205	--	°C	ISO 75-2/A
Peak Melting Temperature	220	--	°C	ASTM D3418, ISO 3146
CLTE - Flow	3.8E-5	--	cm/cm/°C	ASTM E831

Electrical	Dry	Conditioned	Unit	Test Method
Volume Resistivity
1.50 mm	> 1.0E+13	--	ohms·cm	ASTM D257
--	> 1.0E+15	--	ohms·cm	IEC 60093

Additional Information	Dry	Conditioned	Unit	Test Method
Drop Weight Impact Strength (23°C)	4.07	--	J	Internal Method

Category:	Nylon 6 , Polyamide 6
Manufacturer:	BASF Corporation
Trademark:	Ultramid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	1GrwWx_Ultramid-8233G-HS-BK-106.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Tarflen® SM2	Grupa Azoty S.A.	PTFE	Tarflen®
Abstron SE-22M	Bhansali Engineering Polymers Limited	ABS	Abstron
Badadur® PBT7	Bada AG	PBT	Badadur®
Andur 1-83 AP/Curene® 442	Anderson Development Company	PUR-Ether/TDI	Andur
Petrothene® NA942000	LyondellBasell Industries	LDPE	Petrothene®