| PPA, 30% carbon fiber reinforced, heat stabilized, black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.80 | % | Internal method |
| Flow direction | 0.10 | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.7 | % | ISO 62 |
| Moisture Content | % | ISO 15512 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | Low |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 25000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 275 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | °C | ISO 75-2/A |
| Melting Temperature 1 | 315 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+3 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Processing (Melt) Temp | 320 - 340 | °C | |
| Mold Temperature | 140 - 180 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa |
| Injection instructions |
|---|
| Pre-drying is not necessary for materials in moisture proof closed bags. |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAFIN™ P730HG | Mando Advanced Materials Co., Ltd. | PP, Unspecified | TEKAFIN™ |
| TAROLON 3020 | Taro Plast S.p.A. | PC | TAROLON |
| 4MID® 25B20400 | 4Plas | Nylon 6 | 4MID® |
| Karina GRAY PVC COMPOUND 651D18/408-B-IS-SD-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plenco 06343 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |