LNP™ THERMOCOMP™ 5C003 compound
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1GTeQh_LNP-THERMOCOMP-5C003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* 5C003 is a compound based on Polyvinylidene Fluoride resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound FP-VC-1003 Product reorder name: 5C003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 to 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 to 1.3 | % | ASTM D955 |
| Across Flow : 24 hr | 1.2 | % | ISO 294-4 |
| Flow : 24 hr | 0.36 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.030 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 14300 | MPa | ASTM D638 |
| -- | 14500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 78.5 | MPa | ASTM D638 |
| Break | 67.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 0.80 | % | ASTM D638 |
| Break | 0.60 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 11800 | MPa | ASTM D790 |
| -- | 20900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 128 | MPa | ASTM D790 |
| -- | 147 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D4812 |
| 23°C 3 | 15 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 11.4 | J | ASTM D3763 |
| -- | 3.01 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 166 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 165 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 159 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 156 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 210 to 225 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 215 to 230 | °C | |
| Mold Temperature | 65.0 to 90.0 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V74C | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| Spartech Polycom SC14-1213L | Spartech Polycom | Nylon 66 | Spartech |
| Spartech Polycom SCR7-7022R | Spartech Polycom | PC | Spartech |
| Gallonprene® GP520-9011 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Osterlene® LLM1018SA | Osterman & Company | LLDPE | Osterlene® |