Amodel® A-8940 HS Datasheet,PPA,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Amodel® A-8940 HS is a 40% glass-fiber-reinforced, heat-stabilized polyphthalamide (PPA) with a high heat deflection temperature and very high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. Black: A-8940 HS BK 328

General Information
Filler / Reinforcement	Glass fiber reinforced material, 40% filler by weight
Additive	heat stabilizer
Features	Good dimensional stability Low hygroscopicity Rigidity, high Rigid, good High strength High temperature strength Good creep resistance Good chemical resistance Heat resistance, high
Uses	Electrical appliances Industrial application Machine/mechanical parts Metal substitution Connector Automotive Electronics Application in Automobile Field Shell Consumer goods application field
Appearance	Black
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.57	g/cm³	ISO 1183/A
Molding Shrinkage			ASTM D955
Flow	0.34	%	ASTM D955
Transverse flow	0.68	%	ASTM D955
Water Absorption (24 hr)	0.15	%	ASTM D570

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	15100	MPa	ISO 527-2
Tensile Stress (Break, 23°C)	243	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	2.0	%	ISO 527-2
Flexural Modulus (23°C)	14500	MPa	ISO 178
Flexural Strength (Break, 23°C)	357	MPa	ISO 178
Flexural Strain at Break (23°C)	2.6	%	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	9.5	kJ/m²	ISO 179/1eA
23°C	9.7	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	59	kJ/m²	ISO 179/1eU
23°C	60	kJ/m²	ISO 179/1eU
Notched Izod Impact (23°C)	10	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength			ISO 180/A
-30°C	55	kJ/m²	ISO 180/A
23°C	59	kJ/m²	ISO 180/A

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	311	°C	ISO 75-2/Bf
1.8 MPa, not annealed	293	°C	ISO 75-2/Af
Melting Temperature	323	°C	ISO 11357-3

Injection	Nominal Value	Unit
Drying Temperature	120	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.030 - 0.060	%
Rear Temperature	316 - 329	°C
Middle Temperature	316 - 329	°C
Front Temperature	324 - 335	°C
Processing (Melt) Temp	321 - 343	°C
Mold Temperature	170	°C

Injection instructions
Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Injection instructions

Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	1GPsdQ_Amodel-A-8940-HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Polytron® P40B11	Polyram Ram-On Industries	PP Homopolymer	Polytron®
SABIC® PPcompound 7795	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound
Nylene® 4114-14	Custom Resins Group	Nylon 66	Nylene®
DIC.PPS FZ-1130-D5	DIC Corporation	PPS	DIC.PPS
LNP™ STAT-KON™ DX04490 compound	SABIC Innovative Plastics	PC	LNP™ STAT-KON™