NORYL™ SE1X resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1GGMeQ_NORYL-SE1X-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V1, UL746C F1. Dielectric strength. Suitable for E/E market indoor/outdoor applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 8.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 8.70 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow 1 | 0.50 to 0.70 | % | |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2500 | MPa | ASTM D638 |
| -- | 2670 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 65.0 | MPa | ASTM D638 |
| Yield | 61.3 | MPa | ISO 527-2/50 |
| Break 4 | 53.1 | MPa | ASTM D638 |
| Break | 50.8 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 4.0 | % | ASTM D638 |
| Yield | 4.3 | % | ISO 527-2/50 |
| Break 6 | 15 | % | ASTM D638 |
| Break | 21 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 2700 | MPa | ASTM D790 |
| 100 mm Span 8 | 2400 | MPa | ASTM D790 |
| -- 9 | 2560 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 99.5 | MPa | ISO 178 |
| Yield, 50.0 mm Span 10 | 100 | MPa | ASTM D790 |
| Yield, 100 mm Span 11 | 98.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -30°C | 110 | J/m | ASTM D256 |
| 23°C | 180 | J/m | ASTM D256 |
| 23°C 12 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 2600 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 49.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 127 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 6.40 mm | 129 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 13 | 129 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 113 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 118 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 14 | 115 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 132 | °C | ISO 306/B50 |
| -- | 135 | °C | ISO 306/B120 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.8E-5 | cm/cm/°C | |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI Str | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 2.3E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 2.52 | ||
| 60 Hz | 2.52 | ||
| 1 MHz | 2.46 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 3.4E-3 | ||
| 60 Hz | 3.4E-3 | ||
| 1 MHz | 2.1E-3 | ||
| Arc Resistance 15 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.47 mm | V-1 | ||
| 5.99 mm | V-0 | ||
| Radiant Panel Listing (UL) | RP100 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 249 to 299 | °C | |
| Middle Temperature | 260 to 304 | °C | |
| Front Temperature | 271 to 310 | °C | |
| Nozzle Temperature | 282 to 310 | °C | |
| Processing (Melt) Temp | 282 to 310 | °C | |
| Mold Temperature | 76.7 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.6 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 2.6 mm/min |
| 12 . | 80*10*4 |
| 13 . | 120*10*4 mm |
| 14 . | 120*10*4 mm |
| 15 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® A3U40G5 | BASF Corporation | Nylon 66 | Ultramid® |
| Forprene® 6NB901A90 | SO.F.TER. SPA | TPV | Forprene® |
| Geon™ Vinyl Wire & Cable WEAC31L | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Kepital® F10-03H M | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| HydroMed™ D3 | AdvanSource Biomaterials Corp. | PUR-Ether | HydroMed™ |