RIALGLASS C 07 S 30 G
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALGLASS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1FHeEO_RIALGLASS-C-07-S-30-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene elastomerized heterphasic copolymer 30% glass fiber reinforced; base thermal stabilization; good stiffness and thermal properties; wide impact strength interval, up to -40°C. Flowability specific for injection molding; available in versions natural and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.95 | % | |
| Flow | 0.25 | % | |
| Ash Content | 30 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 61.0 | MPa | |
| Break, 23°C | 60.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | 5.0 | % | |
| Flexural Modulus 1(23°C) | 4800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 92.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 7.0 | kJ/m² | |
| -20°C | 9.0 | kJ/m² | |
| 23°C | 17 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 135 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 103 | °C | ISO 306/B50 |
| Ball Pressure Test | Pass | IEC 335 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® P grey homopolymer | Röchling Engineering Plastics SE & Co. KG | PP Homopolymer | POLYSTONE® |
| Sylvin 9740-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Monprene® CP-22442 | Teknor Apex Company | TPE | Monprene® |
| AIE PPO 9010F-S085A | Asia International Enterprise (Hong Kong) Limited | PPE+PS | AIE PPO |
| LNP™ STAT-KON™ EE003XXC compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |