POTICON BT212N
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Otsuka Chemical Co., Ltd. |
| Trademark: | POTICON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1Ekce0_POTICONBT212N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The Poticon series features a potassium titanate micro-filler compounded in thermoplastic resins to provide outstanding micro-reinforcement and dimensional stability. The excellent surface smoothness of these compounds limits friction toward opposing materials, reducing wear and allowing for greaseless applications. Moreover, as Poticon diminishes damage toward the mold and metal die and offers excellent recyclability, it also decreases processing costs. Advantages
Applications
BT212N Property: Slide, Flame resistance |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow | 1.8 | % | |
| Transverse flow | 2.0 | % | |
| Water Absorption (Equilibrium) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 78 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 69.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 3900 | MPa | ASTM D790 |
| Flexural Strength | 108 | MPa | ASTM D790 |
| Coefficient of Friction (vs. Steel - Dynamic) | 0.20 | ||
| Abrasion Loss | |||
| -- 1 | 1.00 | 10^-3 mm³/N·km | |
| of counterpart 2 | 0.00 | 10^-3 mm³/N·km |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Distortion | 150 | °C | ASTM D648 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 31 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 8.4E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | Surface pressure: 1MPa |
| 2 . | Slipping velocity: 0.3m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ALC-55D-B30 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| Spartech Polycom PE4120 | Spartech Polycom | HDPE, HMW | Spartech |
| POLYfill PPH K20020 D | Polykemi AB | PP Homopolymer | POLYfill |
| Sylvin 2900-90 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8499-92 Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |