DAUNYL B R300
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Daunia Trading srl |
| Trademark: | DAUNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1E3wGa_DAUNYL-B-R300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DAUNYL B R300 is a polyamide 6 reinforced with 30% glass fibre for injection moulding. It presents high mechanical properties and outstanding dimensional stability. The standard colours are natural and black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.34 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ||||
| Flow | 0.25 to 0.35 | -- | % | ASTM D955 |
| -- | 0.25 to 0.35 | -- | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.85 to 0.95 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | 114 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 5600 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 170 | 100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.5 | 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Strength | 270 | 140 | MPa | ASTM D790, ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 110 | 170 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | -- | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | > 200 | -- | °C | ASTM D1525, ISO 306 |
| Melting Temperature | 217 to 223 | -- | °C | |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Service Temperature | ||||
| Continuous | 80 to 100 | -- | °C | |
| Short Term | 150 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 60 | 40 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | 500 | -- | V | DIN 53480 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide RF006S-GY9A121 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Baoding 69M88 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Argothane® 18247 | Argotec LLC | TPU, Unspecified | Argothane® |
| ESTOPLAST ZK 6002BB02 | Ester Industries Ltd. | PC | ESTOPLAST ZK |
| StarFlex® 7070-1001 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |