XYLEX™ FXY330DF resin
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | XYLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1DuV2S_XYLEXFXY330DFresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyester+PC alloy. Diffusion Effect. Color package may affect performance. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Transverse flow : 3.20mm | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.70 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.27 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1440 | MPa | ASTM D638 |
| -- | 1580 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 47.0 | MPa | ASTM D638 |
| Yield | 49.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 49.0 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | > 5.0 | % | ISO 527-2/50 |
| Fracture 5 | 170 | % | ASTM D638 |
| Fracture | > 200 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 1500 | MPa | ASTM D790 |
| -- 7 | 1600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 77.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 67.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 55 | J/m | ASTM D256 |
| 0°C | 64 | J/m | ASTM D256 |
| 23°C | 70 | J/m | ASTM D256 |
| -30°C 10 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 7.0 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 60.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 72.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 78.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 90.0 | °C | ASTM D1525 13 |
| -- | 92.0 | °C | ISO 306/B50 |
| -- | 93.0 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 8.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 9.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 66 - 77 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 238 - 249 | °C | |
| Middle Temperature | 238 - 260 | °C | |
| Front Temperature | 243 - 266 | °C | |
| Nozzle Temperature | 243 - 266 | °C | |
| Processing (Melt) Temp | 243 - 266 | °C | |
| Mold Temperature | 43 - 60 | °C | |
| Back Pressure | 0.172 - 0.517 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra HoPP 12 | ResMart | PP Homopolymer | ResMart Ultra |
| Siloxane Masterbatch MB50-010 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| Next Nylon 66 Prime Series PX-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Europrene® 1509 | Versalis S.p.A. | SBR, Emulsion | Europrene® |
| LONGLITE® PBT 5630F-104C | CCP Group | PBT | LONGLITE® PBT |