Hifax CA 7442 A
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1DYcG2_HifaxCA7442A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hifax CA 7442 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell' s proprietary Catalloy process technology. It is primarily used for bumper and exterior trim applications in Automotive but can also be used as a base resin for technical compounds. It has a high impact performance and reduced shrinkage. The material also exhibits good processability. The grade is available in natural pellet form. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Transverse flow | 0.70 | % | Internal method |
| Flow | 0.55 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 19.0 | MPa | ISO 527-2/50 |
| Fracture, 23°C | 17.0 | MPa | ISO 527-2/50 |
| Flexural Modulus - Chord 1(23°C) | 1000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 4.5 | kJ/m² | ISO 179/1eA |
| -30°C | 6.5 | kJ/m² | ISO 179/1eA |
| -20°C | 7.5 | kJ/m² | ISO 179/1eA |
| 23°C | 50 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 86.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 121 | °C | ISO 306/B |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 6610/60 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| SNOLEN® IM 55/59 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| Moplen EPS30R | Shazand (Arak) Petrochemical Corporation | PP Copolymer | Moplen |
| Nylene® 4114-33 GL HS | Custom Resins Group | Nylon 66 | Nylene® |
| Tunhe PBT TH6075 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBT | Tunhe PBT |