LNP™ STAT-KON™ RFD02 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1DG5ZB_LNP-STAT-KON-RFD02-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON RFD02 is a compound based on Nylon 66 resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound RF Product reorder name: RFD02 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.0 to 1.2 | % | ASTM D955 |
| Across Flow : 24 hr | 1.4 to 1.6 | % | ASTM D955 |
| Across Flow : 24 hr | 1.5 | % | ISO 294-4 |
| Flow : 24 hr | 1.1 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8270 | MPa | ASTM D638 |
| -- | 7400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 77.9 | MPa | ASTM D638 |
| Break | 74.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 5.5 | % | ASTM D638 |
| Break | 5.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5520 | MPa | ASTM D790 |
| -- | 6300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 131 | MPa | ASTM D790 |
| -- | 139 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 2 | 3.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D4812 |
| 23°C 3 | 14 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 252 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 256 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 237 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 239 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.7E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1603 | RTP Company | PAS | RTP |
| RTP ESD 1382 TFE 15 | RTP Company | PPS | RTP |
| Celanex® 2002-3 | Celanese Corporation | PBT | Celanex® |
| Felix Compounds Eprene TPO | Felix Compounds | SEBS | Felix Compounds |
| I. Stern 6500 | I. STERN & CO. INC. | PS (MIPS) | I. Stern |