TAISOX 3225
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1Ct3B9_TAISOX-3225.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 3225 is a linear low density polyethylene material,. This product is available in North America, Europe or Asia Pacific region. The processing method is: cast film. The main characteristics of TAISOX 3225 are puncture resistance. Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 20 µm, cast film | 147 | MPa | ASTM D882 |
| 1% secant, TD : 20 µm, cast film | 206 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm, extruded film | 9.81 | MPa | ASTM D882 |
| TD : Yield, 20 µm, extruded film | 10.8 | MPa | ASTM D882 |
| MD : Fracture, 20 µm, extruded film | 35.3 | MPa | ASTM D882 |
| TD : Fracture, 20 µm, extruded film | 27.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 20 µm, extruded film | 600 | % | ASTM D882 |
| TD : Fracture, 20 µm, extruded film | 800 | % | ASTM D882 |
| Dart Drop Impact (20 µm, Cast Film) | 120 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm, cast film | 88 | g | ASTM D1922 |
| TD : 20 µm, cast film | 240 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Melting Temperature | 122 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 96 | ASTM D2457 | |
| Clarity | 95.0 | ASTM D1746 | |
| Haze (20.0 µm, Cast Film) | 3.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Blow Up Ratio: 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sicoflex S358 | Ravago Group | ABS | Sicoflex |
| THERMOLAST® K TC5FRN (Series: FR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| ESTOPLAST XU 425 HG36 | Ester Industries Ltd. | Nylon, Unspecified | ESTOPLAST XU |
| Hostalen GF 9045 F | LyondellBasell Industries | HDPE, MMW | Hostalen |
| PLUSTEK PA840G6 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |