DENKA ABS GR-2030G
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1CnXeu_DENKA-ABS-GR-2030G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DENKA ABS GR-2030G is an Acrylonitrile Butadiene Styrene (ABS) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.26 | g/cm³ | ASTM D792 |
| 23°C | 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.10 to 0.30 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 122 | ASTM D785 | |
| R-Scale | 119 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 108 | MPa | ASTM D638 |
| -- | 7980 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 94.0 | MPa | |
| Break | 94.0 | MPa | |
| Nominal Tensile Strain at Break | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 687 | MPa | ASTM D790 |
| -- 3 | 7920 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 147 | MPa | ASTM D790 |
| -- 5 | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed 6 | 105 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 104 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 113 | °C | ASTM D1525 7 |
| -- | 110 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 15 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 15 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Edgewise |
| 7 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aquamix™ 110 | PolyOne Corporation | Latex | Aquamix™ |
| FireCon™ CPE 30-20 RoHS Natural | PolyOne Corporation | CPE | FireCon™ |
| Hostacom EKS360N | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| OnForce™ LFT AM-30LCF/001 Grey | PolyOne Corporation | PPA | OnForce™ LFT |
| neogol® A60 2 Z005 | API SpA | TPO (POE) | neogol® |