Zytel® HTN 51G15HSL NC010
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1CSWaO_Zytel-HTN-51G15HSL-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% Glass Reinforced, PPA, High Performance Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.30 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.40 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6500 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.1 | -- | % | ISO 527-2 |
| Flexural Modulus | 5700 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 6.0 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 25 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 6.0 | -- | kJ/m² | |
| 23°C | 6.0 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 276 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 254 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 300 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 3.0E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 5.7E-5 | -- | cm/cm/°C | |
| Transverse | 6.4E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 3.0E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 7.7E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V926 BLK580 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| POLYMAN® (SAN) 24/5 | A. Schulman Europe | SAN | POLYMAN® |
| Cri-Line LS-918 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| HAIPLEN EP100 K10 BA | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Karina IVORY PVC COMPOUND - E-90901-35/ 1-D-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |