Lupox® TE5000LZ
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupox® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1BeTsK_Lupox-TE5000LZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Impact, Dimensional Stability, Good Weatherability Application Automotive(Door Garnish) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 to 1.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 56.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 100 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2110 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 79.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm | 170 | J/m | |
| 23°C, 6.40 mm | 690 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 115 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 105 | °C | |
| Peak Melting Temperature | 223 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 250 to 260 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 255 to 265 | °C | |
| Nozzle Temperature | 260 to 270 | °C | |
| Processing (Melt) Temp | 260 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.5 mm/min |
| 4 . | 2.5 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7100 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| NuSil MED-4055 | NuSil Technology | Rubber | NuSil |
| Karina MBU GREEN -E 40/587-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MACOMASS PP MM-PP HK 82 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |
| Cellasto® MH24-55 | BASF Polyurethanes GmbH | TPU, Unspecified | Cellasto® |