Clariant Nylon 6/6 66G13-L
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant Nylon 6/6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1BcUe9_Clariant-Nylon-6-6-66G13-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Clariant Nylon 6/6 66G13-L is a Polyamide 66 (Nylon 66) material filled with 13% glass fiber. It is available in North America. Primary attribute of Clariant Nylon 6/6 66G13-L: Lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 4480 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 252 | °C | |
| 1.8 MPa, Unannealed | 238 | °C | |
| Melting Temperature | 257 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANLENE® LDF 200YY | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| Trovidur® EC | Röchling Engineering Plastics SE & Co. KG | PVC, Rigid | Trovidur® |
| Karina GRAY COLOR CONCENTRATE 18/ 91-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina IVORY PVC COMPOUND -E 105900-35/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom TKC 2007N | LyondellBasell Industries | PP Copolymer | Hostacom |