Order Products : sales@su-jiao.com
LAMIGAMID® 700
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Schwartz Technical Plastic |
| Trademark: | LAMIGAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ACKqR_LAMIGAMID-700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
|
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.0 | % | ISO 62 |
| Saturated, 23°C | > 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 57.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 39.0 | MPa | ISO 527-2 |
| Fracture | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 450 | % | ISO 527-2 |
| Flexural Modulus | 790 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 20% strain | 32.0 | MPa | ISO 604 |
| 10% strain | 25.0 | MPa | ISO 604 |
| 5% strain | 16.0 | MPa | ISO 604 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.020 - 0.080 | ASTM D1894 | |
| With steel-static | 0.29 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ISO 180 | |
| Unnotched Izod Impact Strength | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 136 | °C | ISO 3146 |
| CLTE - Flow (20 to 100°C) | 2.0E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 2300 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.33 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Dielectric Strength | 100 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 2.30 | IEC 60250 | |
| Dissipation Factor | 1.0E-4 | IEC 60250 |
| Additional Information |
|---|
| Creep Rate Stress, DIN 53444, 1% Elongation: 3.2 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: 5 N/mm²Friction Wear: 1.0 µm/KmCoef of Friction, ASTM D1894, vs. Steel-Dynamic: 0.02 to 0.08Penetration Resistance, DIN 53482: 1E17 ohm-cmCreepage/leakage Resistance: KA3cThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 120°CSafe Temperature Range, permanent: -100° to 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Qenos PP PPR 1060F | Qenos Pty Ltd | PP Homopolymer | Qenos PP |
| RheTech Polypropylene CC20P200-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| APEX® 3311-60NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Five Plus™ HPP40T | Noble Polymers | PP Homopolymer | Five Plus™ |
| Sylvin 9600-95 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |