TECHNYL® B 218L V20 BLACK 44 N
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 19agDO_TECHNYL-B-218L-V20-BLACK-44-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Copolyamide 66/6, reinforced with 20% of glass fibre, for injection moulding, heat stabilized with improved UV ageing resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.29 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.60 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.2 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.750 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7000 | 4500 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 140 | 85.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 3.0 | 9.0 | % | ISO 527-2/1A |
| Flexural Modulus | 5800 | 3500 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 45 | 83 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 8.0 | 13 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 230 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 242 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 3.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 3.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 32 | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.010 | 0.11 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- | ||
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1776 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SILPURAN® 6610/70 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| PLEXIGLAS® Sheet Optical RP Daylight 99561 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |
| Optix® CA-41 UVT | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |
| Sylvin 8200-60 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |