Chemlon® N60AHY
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 18zvCb_Chemlon-N60AHY.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| N60AHY is a high viscosity, unfilled, heat stabilised grade of nylon 6. It is primarily intended for extrusion applications such as pipe and profile. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 1.2 - 2.0 | -- | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 900 | MPa | ISO 527-2 |
| Tensile Stress | 70.0 | 40.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2600 | 800 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 80.0 | 25.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 11 kJ/m² | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 190 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 95.0 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 14 | 10 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 230 - 250 | °C | |
| Cylinder Zone 3 Temp. | 240 - 260 | °C | |
| Cylinder Zone 5 Temp. | 240 - 260 | °C | |
| Melt Temperature | 240 - 270 | °C |
| Extrusion instructions |
|---|
| No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2740 S-30A | RTP Company | SEBS | RTP |
| Tecotek® PC44 GR003 ZG70 | Eurotec Engineering Plastics | PC | Tecotek® |
| Dynalloy™ OBC8000-T40 | PolyOne Corporation | TPE | Dynalloy™ |
| Grivory® GTR 45 | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| OTECH TPO OTR8588 - Cord Jacket | OTECH Corporation | TPO | OTECH TPO |