Iupiace® AP6GM2
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupiace® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 18dgu2_Iupiace-AP6GM2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupiace® AP6GM2 is a Polyphenylene Ether + PS (PPE+PS) material filled with 20% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupiace® AP6GM2 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 28.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Water Absorption (Saturation, 23°C) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.9 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 116 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 4.7E-5 | cm/cm/°C | |
| Transverse | 5.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 5.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 250 to 290 | °C | |
| Front Temperature | 250 to 290 | °C | |
| Nozzle Temperature | 250 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergadur™ PB400 G30 UF UV | PolyOne Corporation | PBT | Bergadur™ |
| EXCELLOY TK12G20 | Techno Polymer Co, Ltd. | ABS+PBT | EXCELLOY |
| Karina CLEAR PVC COMPOUND 50/201-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ AB002 compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |
| Peripor® 300 E | BASF Corporation | PS (EPS) | Peripor® |