TECHNYL® A 218W V30 BLACK FA
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 18Yu3e_TECHNYL-A-218W-V30-BLACK-FA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, reinforced with 30% of glass fibre, for injection moulding, heat stabilized, with improved hydrolysis resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.80 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.620 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 7500 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 185 | 130 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 3.0 | 4.0 | % | ISO 527-2/1A |
| Flexural Modulus | 9000 | 6400 | MPa | ISO 178 |
| Flexural Stress | 275 | 180 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 11 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 80 | 90 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 10 | 17 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 255 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 2.8E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 3.30 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.080 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index (1.60 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1930D | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Rainmaker Polypropylene MCCPMI40 | Rainmaker Polymers LLC | PP Copolymer | Rainmaker Polypropylene |
| EPOXIDUR® EP 3580 | RASCHIG GmbH | Epoxy | EPOXIDUR® |
| LUVOCOM® 50-1396 | Lehmann & Voss & Co. | PC | LUVOCOM® |
| MAXATEL® AH100P-NC010 | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | MAXATEL® |