URE-BOND® II
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | URE-BOND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 18VX1o_URE-BOND-II.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| URE-BOND® II is a premium performance urethane adhesive compound that offers a strong flexible bond between many different surfaces. URE-BOND® is ideal for adhering polyurethane rubber and other polymer products to many types of substrates (such as plaster, wood, cement, stone) and non-porous materials (such as glass, hard plastics and a variety of metals). URE-BOND® II has also been used to repair torn polyurethane molds on a limited basis (with proper surface preparation). Working time is 5 minutes at room temperature (73° F / 23° C). Once mixed and applied, URE-BOND® takes about 60 minutes to cure and yields a strong, flexible bond. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Specific Volume | 0.903 | cm³/g |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Handle Time (23°C) | 1.0 | hr | |
| Mixing Ratio | 1A:1B by volume |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4.83 | MPa | ASTM D638 |
| Tensile Strength (Break) | 5.52 | MPa | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 23.4 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 120 | % | ASTM D412 |
| Tear Strength 1 | 30.6 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 5.0 | min | |
| Thermoset Mix Viscosity | 5400 | cP | ASTM D2393 |
| Demold Time (23°C) | 1400 | min |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 209 K FR | RTP Company | PARA | RTP |
| ULTEM™ XH6050 resin | SABIC Innovative Plastics Asia Pacific | PEI | ULTEM™ |
| Hostaform® C 9021 TF5 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Hostacom HC ERC 342N | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| NORYL™ SE1GFN3 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |