Terluran® GP-22

Category:	ABS , Acrylonitrile Butadiene Styrene
Manufacturer:	INEOS Styrolution Group GmbH
Trademark:	Terluran®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	17FGAA_Terluran-GP-22.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Terluran GP-22 is an easy-flow, general purpose injection molding grade with high resistance to impact and heat distortion; intended for a wide range of applications, particularly in the housings sector.

General Information
Features	General Purpose Good Colorability Good Impact Resistance Good Surface Finish High Gloss Medium Flow
Uses	Appliances Automotive Applications General Purpose Household Goods Housings Sanitary Products Toys
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.04	g/cm³	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR)			ASTM D1238
200°C/5.0 kg	1.5	g/10 min
220°C/10.0 kg	19	g/10 min
Melt Volume-Flow Rate (MVR)
230°C/3.8 kg	4.80	cm³/10min	ASTM D1238
220°C/10.0 kg	19.0	cm³/10min	ISO 1133
Molding Shrinkage
Flow	0.40 to 0.70	%	ASTM D955
--	0.40 to 0.70	%	ISO 294-4
Water Absorption
Saturation, 23°C	1.0	%	ASTM D570, ISO 62
Equilibrium, 23°C, 50% RH	0.22	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	103		ASTM D785
Ball Indentation Hardness	97.0	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2300	MPa	ASTM D638, ISO 527-2
Tensile Strength (Yield, 23°C)	45.0	MPa	ASTM D638, ISO 527-2
Tensile Strain
Yield, 23°C	2.6	%	ISO 527-2
Break	2.6	%	ASTM D638
Nominal Tensile Strain at Break (23°C)	10	%	ISO 527-2
Flexural Modulus	2300	MPa	ASTM D790
Flexural Strength	65.0	MPa	ASTM D790, ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179
-30°C	8.0	kJ/m²
23°C	22	kJ/m²
Charpy Unnotched Impact Strength			ISO 179
-30°C	100	kJ/m²
23°C	180	kJ/m²
Notched Izod Impact
-30°C	59	J/m	ASTM D256
-18°C	100	J/m	ASTM D256
23°C	300	J/m	ASTM D256
-30°C	8.0	kJ/m²	ISO 180/A
23°C	26	kJ/m²	ISO 180/A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed	90.6	°C	ASTM D648
0.45 MPa, Annealed	104	°C	ASTM D648
0.45 MPa, Annealed	99.0	°C	ISO 75-2/B
1.8 MPa, Unannealed	77.8	°C	ASTM D648
1.8 MPa, Annealed	98.9	°C	ASTM D648
1.8 MPa, Annealed	94.0	°C	ISO 75-2/A
Vicat Softening Temperature
--	105	°C	ISO 306/A50
--	96.0	°C	ISO 306/B50
CLTE - Flow	8.0E-5 to 1.1E-4	cm/cm/°C	ISO 11359-2
Thermal Conductivity	0.17	W/m/K	DIN 52612

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+13	ohms	IEC 60093
Volume Resistivity
--	> 1.0E+15	ohms·cm	ASTM D257
--	1.0E+15	ohms·cm	IEC 60093
Dielectric Constant
1.00 mm, 1 MHz	2.80		ASTM D150
100 Hz	2.90		IEC 60250
1 MHz	2.80		IEC 60250
Dissipation Factor			IEC 60250
100 Hz	4.8E-3
1 MHz	7.9E-3

Optical	Nominal Value	Unit	Test Method
Yellowness Index	13	YI	DIN 6167

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	2.0 to 4.0	hr
Processing (Melt) Temp	220 to 260	°C
Mold Temperature	30.0 to 60.0	°C
Injection Velocity	200	mm/sec

Resin Grade	Manufacturer	Category	Trademark
RTP 199 X 138789 EG	RTP Company	PP, Unspecified	RTP
DURACON® M140-44	Polyplastics Co., Ltd.	Acetal (POM) Copolymer	DURACON®
Hostacom TRC 352N	LyondellBasell Industries	Polyolefin, Unspecified	Hostacom
Karina CLEAR PVC COMPOUND 84/200-D-AT-IS-SI	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LNP™ THERMOCOMP™ RF0069XZ compound	SABIC Innovative Plastics	Nylon 66	LNP™ THERMOCOMP™