Geon™ Vinyl Rigid Extrusion 87345
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Rigid Extrusion |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 16udoV_Geon-Vinyl-Rigid-Extrusion-87345.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon™ Vinyl Rigid Extrusion 87345 is a Rigid Polyvinyl Chloride product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Plumbing/Piping/Potable Water. Primary characteristic: chemical resistant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 13454 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2990 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 49.0 | MPa | ASTM D638 |
| Flexural Modulus | 3190 | MPa | ASTM D790 |
| Flexural Strength | 98.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| 23°C, 3.18 mm, Injection Molded | 80 | J/m | |
| Across Flow : 23°C, 3.18 mm, Compression Molded | 64 | J/m | |
| Flow : 23°C, 3.18 mm, Compression Molded | 59 | J/m | |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 69.4 | J/cm | |
| 23°C 4 | 199 | J/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 75.6 | °C | ASTM D648 |
| CLTE - Flow | 6.1E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Good |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 to 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Procedure A, C.125 Dart |
| 4 . | Procedure B, C.125 Dart |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 4042 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| ALTECH® PA6 A 1000/310 IM | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| ARBOBLEND® V4 | TECNARO GmbH | Biodeg Polymers | ARBOBLEND® |
| Estane® 5713 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| Plenco 05118 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |